C75400 Nickel Silver vs. C19100 Copper
Both C75400 nickel silver and C19100 copper are copper alloys. They have 67% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C75400 nickel silver and the bottom bar is C19100 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.0 to 43 | |
| 17 to 37 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 46 | |
| 43 |
| Shear Strength, MPa | 250 to 370 | |
| 170 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 630 | |
| 250 to 630 |
| Tensile Strength: Yield (Proof), MPa | 130 to 590 | |
| 75 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1080 |
| Melting Onset (Solidus), °C | 1040 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 36 | |
| 250 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 55 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.4 | |
| 56 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 33 |
| Density, g/cm3 | 8.5 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 59 | |
| 43 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 120 | |
| 60 to 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 to 1450 | |
| 24 to 1310 |
| Stiffness to Weight: Axial, points | 7.9 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 7.7 to 20 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 9.9 to 18 |
| Thermal Diffusivity, mm2/s | 11 | |
| 73 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 8.9 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 63.5 to 66.5 | |
| 96.5 to 98.6 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 14 to 16 | |
| 0.9 to 1.3 |
| Phosphorus (P), % | 0 | |
| 0.15 to 0.35 |
| Tellurium (Te), % | 0 | |
| 0.35 to 0.6 |
| Zinc (Zn), % | 16.2 to 22.5 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |