C76200 Nickel Silver vs. Steatite
C76200 nickel silver and steatite belong to fundamentally different material chemistries. C76200 nickel silver is a metal, while steatite is a ceramic material. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 14 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C76200 nickel silver and the bottom bar is steatite.
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 120 | |
68 to 120 |
Poisson's Ratio | 0.31 | |
0.23 |
Tensile Strength: Ultimate (UTS), MPa | 390 to 790 | |
60 to 220 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 170 | |
750 to 1230 |
Specific Heat Capacity, J/kg-K | 390 | |
850 to 860 |
Thermal Conductivity, W/m-K | 45 | |
1.8 to 2.5 |
Thermal Expansion, µm/m-K | 19 | |
7.0 to 9.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.2 | |
1.9 to 2.8 |
Common Calculations
Stiffness to Weight: Axial, points | 7.8 | |
14 to 32 |
Stiffness to Weight: Bending, points | 20 | |
52 to 83 |
Strength to Weight: Axial, points | 13 to 27 | |
6.4 to 32 |
Strength to Weight: Bending, points | 14 to 23 | |
13 to 42 |
Thermal Diffusivity, mm2/s | 14 | |
0.79 to 1.1 |
Thermal Shock Resistance, points | 13 to 26 | |
5.1 to 33 |