N07041 Nickel vs. Grade CW12MW Nickel
Both N07041 nickel and grade CW12MW nickel are nickel alloys. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is grade CW12MW nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 220 |
| Elongation at Break, % | 14 | |
| 4.6 |
| Fatigue Strength, MPa | 540 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 560 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 310 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 410 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 9.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 220 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 47 | |
| 17 |
| Strength to Weight: Bending, points | 34 | |
| 17 |
| Thermal Shock Resistance, points | 38 | |
| 16 |