N07041 Nickel vs. Nickel 625
Both N07041 nickel and nickel 625 are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is nickel 625.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 33 to 34 |
| Fatigue Strength, MPa | 540 | |
| 240 to 320 |
| Shear Strength, MPa | 850 | |
| 530 to 600 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 790 to 910 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 320 to 450 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 440 |
| Thermal Conductivity, W/m-K | 11 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.6 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 220 to 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 260 to 490 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 | |
| 26 to 29 |
| Strength to Weight: Bending, points | 34 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 2.9 |
| Thermal Shock Resistance, points | 38 | |
| 22 to 25 |