N07041 Nickel vs. R30008 Cobalt
N07041 nickel belongs to the nickel alloys classification, while R30008 cobalt belongs to the cobalt alloys. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is R30008 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 210 |
| Elongation at Break, % | 14 | |
| 1.1 to 73 |
| Fatigue Strength, MPa | 540 | |
| 320 to 530 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 950 to 1700 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 500 to 1080 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.4 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 590 to 2720 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 47 | |
| 31 to 56 |
| Strength to Weight: Bending, points | 34 | |
| 25 to 37 |
| Thermal Shock Resistance, points | 38 | |
| 25 to 44 |