WE54A Magnesium vs. EN AC-21200 Aluminum
WE54A magnesium belongs to the magnesium alloys classification, while EN AC-21200 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is WE54A magnesium and the bottom bar is EN AC-21200 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 85 | |
| 120 to 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 71 |
| Elongation at Break, % | 4.3 to 5.6 | |
| 3.9 to 6.2 |
| Fatigue Strength, MPa | 98 to 130 | |
| 110 to 130 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 270 to 300 | |
| 410 to 440 |
| Tensile Strength: Yield (Proof), MPa | 180 | |
| 270 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 660 |
| Melting Onset (Solidus), °C | 570 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 960 | |
| 880 |
| Thermal Conductivity, W/m-K | 52 | |
| 130 |
| Thermal Expansion, µm/m-K | 25 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 47 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 10 |
| Density, g/cm3 | 1.9 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 29 | |
| 8.0 |
| Embodied Energy, MJ/kg | 260 | |
| 150 |
| Embodied Water, L/kg | 900 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 to 14 | |
| 16 to 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 380 | |
| 500 to 930 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 62 | |
| 46 |
| Strength to Weight: Axial, points | 39 to 43 | |
| 38 to 40 |
| Strength to Weight: Bending, points | 49 to 51 | |
| 41 to 43 |
| Thermal Diffusivity, mm2/s | 28 | |
| 49 |
| Thermal Shock Resistance, points | 18 to 19 | |
| 18 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 93.3 to 95.7 |
| Copper (Cu), % | 0 to 0.030 | |
| 4.0 to 5.0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Lithium (Li), % | 0 to 0.2 | |
| 0 |
| Magnesium (Mg), % | 88.7 to 93.4 | |
| 0.15 to 0.5 |
| Manganese (Mn), % | 0 to 0.030 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Unspecified Rare Earths, % | 1.5 to 4.0 | |
| 0 |
| Yttrium (Y), % | 4.8 to 5.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.1 |