ZE41A Magnesium vs. EN AC-44100 Aluminum
ZE41A magnesium belongs to the magnesium alloys classification, while EN AC-44100 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ZE41A magnesium and the bottom bar is EN AC-44100 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 63 | |
| 59 |
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 72 |
| Elongation at Break, % | 3.3 | |
| 4.9 |
| Fatigue Strength, MPa | 98 | |
| 64 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 18 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 180 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 87 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 570 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 590 |
| Melting Onset (Solidus), °C | 540 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 900 |
| Thermal Conductivity, W/m-K | 110 | |
| 130 |
| Thermal Expansion, µm/m-K | 27 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 9.5 |
| Density, g/cm3 | 1.9 | |
| 2.5 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 7.7 |
| Embodied Energy, MJ/kg | 170 | |
| 140 |
| Embodied Water, L/kg | 940 | |
| 1050 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.1 | |
| 7.1 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 53 |
| Stiffness to Weight: Axial, points | 13 | |
| 16 |
| Stiffness to Weight: Bending, points | 63 | |
| 55 |
| Strength to Weight: Axial, points | 31 | |
| 19 |
| Strength to Weight: Bending, points | 41 | |
| 27 |
| Thermal Diffusivity, mm2/s | 59 | |
| 58 |
| Thermal Shock Resistance, points | 12 | |
| 8.2 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 84.4 to 89.5 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 | |
| 0 to 0.65 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 91.7 to 95.4 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 0.55 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 | |
| 10.5 to 13.5 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Unspecified Rare Earths, % | 0.75 to 1.8 | |
| 0 |
| Zinc (Zn), % | 3.5 to 5.0 | |
| 0 to 0.15 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.15 |