ZK60A Magnesium vs. 7003 Aluminum
ZK60A magnesium belongs to the magnesium alloys classification, while 7003 aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is ZK60A magnesium and the bottom bar is 7003 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 70 |
| Elongation at Break, % | 4.5 to 9.9 | |
| 11 |
| Fatigue Strength, MPa | 150 to 180 | |
| 130 to 150 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 18 | |
| 26 |
| Shear Strength, MPa | 170 to 190 | |
| 210 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 330 | |
| 350 to 390 |
| Tensile Strength: Yield (Proof), MPa | 230 to 250 | |
| 300 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 600 | |
| 630 |
| Melting Onset (Solidus), °C | 550 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 960 | |
| 870 |
| Thermal Conductivity, W/m-K | 120 | |
| 150 |
| Thermal Expansion, µm/m-K | 26 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 to 30 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 9.5 |
| Density, g/cm3 | 1.9 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 8.1 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 940 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 29 | |
| 37 to 41 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 570 to 690 | |
| 630 to 710 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 63 | |
| 47 |
| Strength to Weight: Axial, points | 47 to 49 | |
| 33 to 37 |
| Strength to Weight: Bending, points | 55 to 56 | |
| 37 to 40 |
| Thermal Diffusivity, mm2/s | 66 | |
| 59 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 15 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 90.6 to 94.5 |
| Chromium (Cr), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 92.5 to 94.8 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 4.8 to 6.2 | |
| 5.0 to 6.5 |
| Zirconium (Zr), % | 0.45 to 1.0 | |
| 0.050 to 0.25 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.15 |