Zamak 3 vs. Optical Silicon
Zamak 3 and optical silicon belong to fundamentally different material chemistries. Zamak 3 is a metal, while optical silicon is a ceramic material. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 19 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is Zamak 3 and the bottom bar is optical silicon.
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 410 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 86 | |
| 150 |
| Fracture Toughness, MPa-m1/2 | 12 | |
| 3.5 |
| Knoop Hardness | 110 | |
| 1130 |
| Poisson's Ratio | 0.25 | |
| 0.28 |
| Shear Modulus, GPa | 33 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 110 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 95 | |
| 1350 |
| Melting Onset (Solidus), °C | 380 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 700 |
| Thermal Conductivity, W/m-K | 110 | |
| 150 |
| Thermal Expansion, µm/m-K | 27 | |
| 3.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.4 | |
| 2.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.5 | |
| 35 |
| Stiffness to Weight: Bending, points | 23 | |
| 75 |
| Strength to Weight: Axial, points | 12 | |
| 13 |
| Strength to Weight: Bending, points | 15 | |
| 22 |
| Thermal Diffusivity, mm2/s | 43 | |
| 93 |
| Thermal Shock Resistance, points | 8.6 | |
| 18 |