ZA-12 vs. Nickel 601
ZA-12 belongs to the zinc alloys classification, while nickel 601 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is ZA-12 and the bottom bar is nickel 601.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 200 |
| Elongation at Break, % | 1.6 to 5.3 | |
| 10 to 38 |
| Fatigue Strength, MPa | 73 to 120 | |
| 220 to 380 |
| Poisson's Ratio | 0.26 | |
| 0.28 |
| Shear Modulus, GPa | 33 | |
| 76 |
| Shear Strength, MPa | 240 to 300 | |
| 440 to 530 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 400 | |
| 660 to 890 |
| Tensile Strength: Yield (Proof), MPa | 210 to 320 | |
| 290 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 100 | |
| 1100 |
| Melting Completion (Liquidus), °C | 430 | |
| 1410 |
| Melting Onset (Solidus), °C | 380 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 11 |
| Thermal Expansion, µm/m-K | 24 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 49 |
| Density, g/cm3 | 6.0 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 8.0 |
| Embodied Energy, MJ/kg | 64 | |
| 110 |
| Embodied Water, L/kg | 440 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.0 to 20 | |
| 86 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 620 | |
| 210 to 1630 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 22 to 30 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 20 to 25 |
| Thermal Diffusivity, mm2/s | 43 | |
| 2.8 |
| Thermal Shock Resistance, points | 9.4 to 14 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 10.5 to 11.5 | |
| 1.0 to 1.7 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 21 to 25 |
| Copper (Cu), % | 0.5 to 1.2 | |
| 0 to 1.0 |
| Iron (Fe), % | 0 to 0.075 | |
| 7.7 to 20 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 |
| Magnesium (Mg), % | 0.015 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.020 | |
| 58 to 63 |
| Silicon (Si), % | 0 to 0.060 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Zinc (Zn), % | 87.1 to 89 | |
| 0 |