3003 (AlMn1Cu) Aluminum

Properties

Compare
Bulk Modulus
67 GPa, or 9.7 106 psi
Density
2.73 g/cm3, or 170 lb/ft3
Elastic (Young's) Modulus
69 GPa, or 10 106 psi
Elongation at Break
Typical
10 to 38 %
Elongation at Break
Minimum
1 to 14 %
Elongation at Break
-200°C (-330°F)
24 to 46 %
Elongation at Break
-100°C (-150°F)
19 to 43 %
Elongation at Break
100°C (210°F)
10 to 43 %
Elongation at Break
200°C (390°F)
17 to 59 %
Elongation at Break
300°C (570°F)
67 to 69 %
Elongation at Break
400°C (750°F)
70 %
Fatigue Strength (Endurance Limit)
50 to 70 MPa, or 7.2 to 10 103 psi
Fracture Toughness
48 to 69 MPa-m1/2
Hardness
Brinell
28 to 55
Maximum Temperature
No-Load Shape Stability
180 °C, or 350 °F
Maximum Temperature
Onset of Melting (Solidus)
643 °C, or 1180 °F
Resilience
Unit, Per Volume
Resilience
Ultimate (Unit Rupture Work), Per Volume
Resilience
Unit, Per Mass
Resilience
Ultimate, Per Mass
Shear Modulus
25 GPa, or 3.6 106 psi
Shear Strength
76 to 110 MPa, or 11 to 15 103 psi
Specific Heat Capacity
Conventional
895 J/kg-K
Specific Heat Capacity
Volumetric
2400 103 J/m3-K
Speed of Sound
150 103 m/s, or 490 103 ft/s
Stiffness-to-Weight Ratio
Tensile
25 MN-m/kg
Strength-to-Weight Ratio
Fatigue
18 to 25 kN-m/kg
Strength-to-Weight Ratio
Shear
27 to 40 kN-m/kg
Strength-to-Weight Ratio
Tensile, Ultimate
40 to 73 kN-m/kg
Strength-to-Weight Ratio
Tensile, Yield
15 to 67 kN-m/kg
Tensile Strength
Ultimate
110 to 200 MPa, or 15 to 29 103 psi
Tensile Strength
Ultimate, Maximum
Tensile Strength
Ultimate, Minimum
Tensile Strength
Ultimate, -200°C (-330°F)
Tensile Strength
Ultimate, -100°C (-150°F)
Tensile Strength
Ultimate, 100°C (210°F)
Tensile Strength
Ultimate, 200°C (390°F)
Tensile Strength
Ultimate, 300°C (570°F)
Tensile Strength
Ultimate, 400°C (750°F)
Tensile Strength
Yield (Proof)
42 to 185 MPa, or 6.0 to 26.8 103 psi
Tensile Strength
Yield, Minimum
Tensile Strength
Yield, -200°C (-330°F)
Tensile Strength
Yield, -100°C (-150°F)
Tensile Strength
Yield, 100°C (210°F)
Tensile Strength
Yield, 200°C (390°F)
Tensile Strength
Yield, 300°C (570°F)
Tensile Strength
Yield, 400°C (750°F)
Thermal Conductivity
Ambient
159 to 193 W/m-K
Thermal Expansion
20 to 100°C
23.2 µm/m-K
Thermal Expansion
20 to 200°C
Thermal Expansion
20 to 300°C

Only showing properties for which the substantial majority of variants have data.

See Also

Aluminum Standards and Data, The Aluminum Association Inc., 2006.


ASTM B 209, Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate.


ISO 6361, Wrought Aluminium and Aluminium Alloy Sheets, Strips and Plates.


J. Randolph Kissell and Robert L. Ferry, Aluminum Structures: A Guide to Their Specifications and Design, 2nd ed., 2002 (link).


John E. Hatch (editor), Aluminum: Properties and Physical Metallurgy, 1984 (link).


Mark E. Schlesinger, Aluminum Recycling, 2007 (link).


Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993 (link).

'