5050-H34 Aluminum

Properties

Compare
Bulk Modulus
67 GPa, or 9.7 106 psi
Density
2.69 g/cm3, or 167 lb/ft3
Elastic (Young's) Modulus
69 GPa, or 10 106 psi
Hardness
Brinell
53
Maximum Temperature
Onset of Melting (Solidus)
627 °C, or 1160 °F
Resilience
Unit, Per Volume
Resilience
Unit, Per Mass
Shear Modulus
25.9 GPa, or 3.75 106 psi
Shear Strength
123 MPa, or 17.8 103 psi
Specific Heat Capacity
Conventional
900 J/kg-K
Specific Heat Capacity
Volumetric
2400 103 J/m3-K
Speed of Sound
160 103 m/s, or 520 103 ft/s
Stiffness-to-Weight Ratio
Tensile
25 MN-m/kg
Strength-to-Weight Ratio
Fatigue
33 kN-m/kg
Strength-to-Weight Ratio
Tensile, Ultimate
70 kN-m/kg
Strength-to-Weight Ratio
Tensile, Yield
61 kN-m/kg
Tensile Strength
Ultimate
190 MPa, or 27 103 psi
Tensile Strength
Ultimate, Maximum
Tensile Strength
Ultimate, Minimum
Tensile Strength
Ultimate, -200°C (-330°F)
Tensile Strength
Ultimate, -100°C (-150°F)
Tensile Strength
Ultimate, 100°C (210°F)
Tensile Strength
Ultimate, 200°C (390°F)
Tensile Strength
Ultimate, 300°C (570°F)
Tensile Strength
Ultimate, 400°C (750°F)
Tensile Strength
Yield (Proof)
165 MPa, or 23.9 103 psi
Tensile Strength
Yield, Minimum
Tensile Strength
Yield, -200°C (-330°F)
Tensile Strength
Yield, -100°C (-150°F)
Tensile Strength
Yield, 100°C (210°F)
Tensile Strength
Yield, 200°C (390°F)
Tensile Strength
Yield, 300°C (570°F)
Tensile Strength
Yield, 400°C (750°F)
Thermal Conductivity
Ambient
191 W/m-K
Thermal Expansion
20 to 100°C
23.8 µm/m-K
Thermal Expansion
20 to 200°C
Thermal Expansion
20 to 300°C

See Also

Aluminum Standards and Data, The Aluminum Association Inc., 2006.


ASTM B 209, Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate.


ISO 6361, Wrought Aluminium and Aluminium Alloy Sheets, Strips and Plates.


J. Randolph Kissell and Robert L. Ferry, Aluminum Structures: A Guide to Their Specifications and Design, 2nd ed., 2002 (link).


John E. Hatch (editor), Aluminum: Properties and Physical Metallurgy, 1984 (link).


Mark E. Schlesinger, Aluminum Recycling, 2007 (link).


Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993 (link).

'