1/16-Hard 304 Stainless Steel

1/16-hard AISI 304 is AISI 304 stainless steel in the 1/16-hard temper. It has the second lowest strength and second highest ductility compared to the other variants of AISI 304 stainless steel.

The graph bars on the material properties cards below compare 1/16-hard AISI 304 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

190

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Elongation at Break

39 %

Fatigue Strength

300 MPa 44 x 103 psi

Poisson's Ratio

0.28

Shear Modulus

77 GPa 11 x 106 psi

Shear Strength

420 MPa 61 x 103 psi

Tensile Strength: Ultimate (UTS)

620 MPa 89 x 103 psi

Tensile Strength: Yield (Proof)

350 MPa 51 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

420 °C 790 °F

Maximum Temperature: Mechanical

710 °C 1300 °F

Melting Completion (Liquidus)

1450 °C 2640 °F

Melting Onset (Solidus)

1400 °C 2550 °F

Specific Heat Capacity

480 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

16 W/m-K 9.2 BTU/h-ft-°F

Thermal Expansion

17 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.4 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.7 % IACS

Otherwise Unclassified Properties

Base Metal Price

15 % relative

Calomel Potential

-80 mV

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

3.0 kg CO2/kg material

Embodied Energy

43 MJ/kg 18 x 103 BTU/lb

Embodied Water

150 L/kg 17 gal/lb

Common Calculations

PREN (Pitting Resistance)

20

Resilience: Ultimate (Unit Rupture Work)

210 MJ/m3

Resilience: Unit (Modulus of Resilience)

320 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

22 points

Strength to Weight: Bending

21 points

Thermal Diffusivity

4.2 mm2/s

Thermal Shock Resistance

13 points

Alloy Composition

Iron (Fe)Fe 66.5 to 74
Chromium (Cr)Cr 18 to 20
Nickel (Ni)Ni 8.0 to 10.5
Manganese (Mn)Mn 0 to 2.0
Silicon (Si)Si 0 to 0.75
Nitrogen (N)N 0 to 0.1
Carbon (C)C 0 to 0.080
Phosphorus (P)P 0 to 0.045
Sulfur (S)S 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar

ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

ASTM A276: Standard Specification for Stainless Steel Bars and Shapes

Creep-Resistant Steels, Fujio Abe et al. (editors), 2008

Advanced Materials in Automotive Engineering, Jason Rowe (editor), 2012

ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels

Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002

Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011

Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984

ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994