1/8-Hard 316 Stainless Steel

1/8-hard AISI 316 is AISI 316 stainless steel in the 1/8-hard temper. The graph bars on the material properties cards below compare 1/8-hard AISI 316 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

240

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Elongation at Break

34 %

Fatigue Strength

340 MPa 49 x 103 psi

Poisson's Ratio

0.28

Reduction in Area

80 %

Rockwell B Hardness

80

Shear Modulus

78 GPa 11 x 106 psi

Shear Strength

530 MPa 76 x 103 psi

Tensile Strength: Ultimate (UTS)

790 MPa 110 x 103 psi

Tensile Strength: Yield (Proof)

430 MPa 62 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

410 °C 770 °F

Maximum Temperature: Mechanical

590 °C 1090 °F

Melting Completion (Liquidus)

1400 °C 2550 °F

Melting Onset (Solidus)

1380 °C 2510 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

15 W/m-K 8.9 BTU/h-ft-°F

Thermal Expansion

16 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.6 % IACS

Otherwise Unclassified Properties

Base Metal Price

19 % relative

Calomel Potential

-50 mV

Density

7.9 g/cm3 490 lb/ft3

Embodied Carbon

3.9 kg CO2/kg material

Embodied Energy

53 MJ/kg 23 x 103 BTU/lb

Embodied Water

150 L/kg 18 gal/lb

Common Calculations

PREN (Pitting Resistance)

26

Resilience: Ultimate (Unit Rupture Work)

230 MJ/m3

Resilience: Unit (Modulus of Resilience)

450 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

28 points

Strength to Weight: Bending

24 points

Thermal Diffusivity

4.1 mm2/s

Thermal Shock Resistance

17 points

Alloy Composition

Iron (Fe)Fe 62 to 72
Chromium (Cr)Cr 16 to 18
Nickel (Ni)Ni 10 to 14
Molybdenum (Mo)Mo 2.0 to 3.0
Manganese (Mn)Mn 0 to 2.0
Silicon (Si)Si 0 to 0.75
Nitrogen (N)N 0 to 0.1
Carbon (C)C 0 to 0.080
Phosphorus (P)P 0 to 0.045
Sulfur (S)S 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar

ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

ASTM A276: Standard Specification for Stainless Steel Bars and Shapes

Creep-Resistant Steels, Fujio Abe et al. (editors), 2008

Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012

ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels

Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002

Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011

Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984

Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993