Extra-Hard (H06) C43400 Brass
H06 C43400 brass is C43400 brass in the H06 (extra hard) temper. The graph bars on the material properties cards below compare H06 C43400 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
5.0 %
Poisson's Ratio
0.33
Rockwell B Hardness
83
Rockwell Superficial 30T Hardness
74
Shear Modulus
42 GPa 6.1 x 106 psi
Shear Strength
360 MPa 52 x 103 psi
Tensile Strength: Ultimate (UTS)
580 MPa 84 x 103 psi
Tensile Strength: Yield (Proof)
530 MPa 77 x 103 psi
Thermal Properties
Latent Heat of Fusion
190 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
1020 °C 1870 °F
Melting Onset (Solidus)
990 °C 1810 °F
Specific Heat Capacity
380 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
140 W/m-K 79 BTU/h-ft-°F
Thermal Expansion
19 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
31 % IACS
Electrical Conductivity: Equal Weight (Specific)
32 % IACS
Otherwise Unclassified Properties
Base Metal Price
28 % relative
Density
8.6 g/cm3 540 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
44 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 38 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
28 MJ/m3
Resilience: Unit (Modulus of Resilience)
1270 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
19 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
41 mm2/s
Thermal Shock Resistance
20 points
Alloy Composition
| Cu | 84 to 87 | |
| Zn | 11.4 to 15.6 | |
| Sn | 0.4 to 1.0 | |
| Fe | 0 to 0.050 | |
| Pb | 0 to 0.050 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015