Spheroidized and Cold Drawn (+AC+C) 1.5520 Steel

EN 1.5520 +AC+C steel is EN 1.5520 steel in the spheroidized and cold-drawn condition. It has the lowest ductility compared to the other variants of EN 1.5520 steel. The graph bars on the material properties cards below compare EN 1.5520 +AC+C steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

150

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

11 %

Fatigue Strength

240 MPa 34 x 103 psi

Poisson's Ratio

0.29

Reduction in Area

69 %

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

290 MPa 43 x 103 psi

Tensile Strength: Ultimate (UTS)

490 MPa 71 x 103 psi

Tensile Strength: Yield (Proof)

380 MPa 55 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 760 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

50 W/m-K 29 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.1 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.2 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.9 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.0 x 103 BTU/lb

Embodied Water

48 L/kg 5.7 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

51 MJ/m3

Resilience: Unit (Modulus of Resilience)

380 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

17 points

Strength to Weight: Bending

18 points

Thermal Diffusivity

13 mm2/s

Thermal Shock Resistance

14 points

Alloy Composition

Iron (Fe)Fe 97.7 to 98.9
Manganese (Mn)Mn 0.9 to 1.2
Carbon (C)C 0.15 to 0.2
Silicon (Si)Si 0 to 0.3
Chromium (Cr)Cr 0 to 0.3
Copper (Cu)Cu 0 to 0.25
Phosphorus (P)P 0 to 0.025
Sulfur (S)S 0 to 0.025
Boron (B)B 0.00080 to 0.0050

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

Boron in Steel, S. K. Banerji and J. E. Morral (editors), 1980

EN 10263-4: Steel rod, bars and wire for cold heading and cold extrusion - Part 4: Technical delivery conditions for steels for quenching and tempering

Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015