UNS C90300 (Alloy 1B) Navy-G Tin Bronze

C90300 bronze is a bronze formulated for casting. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. C90300 is the UNS number for this material. Additionally, the common industry name is 88-8-0-4. Older literature may refer to this material as ASTM Alloy 1B, but this is now discouraged.

It has a fairly high thermal conductivity and a moderately high ductility among cast bronzes.

The graph bars on the material properties cards below compare C90300 bronze to: cast bronzes (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

110 GPa 16 x 106 psi

Elongation at Break

22 %

Poisson's Ratio

0.34

Shear Modulus

41 GPa 5.9 x 106 psi

Tensile Strength: Ultimate (UTS)

330 MPa 48 x 103 psi

Tensile Strength: Yield (Proof)

150 MPa 22 x 103 psi

Thermal Properties

Latent Heat of Fusion

190 J/g

Maximum Temperature: Mechanical

170 °C 340 °F

Melting Completion (Liquidus)

1000 °C 1830 °F

Melting Onset (Solidus)

850 °C 1570 °F

Specific Heat Capacity

370 J/kg-K 0.089 BTU/lb-°F

Thermal Conductivity

75 W/m-K 43 BTU/h-ft-°F

Thermal Expansion

18 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

12 % IACS

Electrical Conductivity: Equal Weight (Specific)

12 % IACS

Otherwise Unclassified Properties

Base Metal Price

33 % relative

Density

8.7 g/cm3 540 lb/ft3

Embodied Carbon

3.4 kg CO2/kg material

Embodied Energy

56 MJ/kg 24 x 103 BTU/lb

Embodied Water

370 L/kg 45 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

59 MJ/m3

Resilience: Unit (Modulus of Resilience)

110 kJ/m3

Stiffness to Weight: Axial

7.0 points

Stiffness to Weight: Bending

18 points

Strength to Weight: Axial

11 points

Strength to Weight: Bending

12 points

Thermal Diffusivity

23 mm2/s

Thermal Shock Resistance

12 points

Alloy Composition

Among cast copper alloys, the composition of C90300 bronze is notable for containing a comparatively high amount of tin (Sn) and including sulfur (S). Tin is used to improve strength, bearing properties, and corrosion resistance against certain types of media. It also places certain constraints on cast part design, so as to avoid porosity problems. Sulfur is used to improve machinability at the cost of a decrease in electrical conductivity.

Copper (Cu)Cu 86 to 89
Tin (Sn)Sn 7.5 to 9.0
Zinc (Zn)Zn 3.0 to 5.0
Phosphorus (P)P 0 to 1.5
Nickel (Ni)Ni 0 to 1.0
Lead (Pb)Pb 0 to 0.3
Iron (Fe)Fe 0 to 0.2
Antimony (Sb)Sb 0 to 0.2
Sulfur (S)S 0 to 0.050
Silicon (Si)Si 0 to 0.0050
Aluminum (Al)Al 0 to 0.0050
Residualsres. 0 to 0.6

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

ASTM B271: Standard Specification for Copper-Base Alloy Centrifugal Castings

ASTM B505: Standard Specification for Copper Alloy Continuous Castings

Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001

ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001