1050A-H111 Aluminum vs. 5182-H111 Aluminum

Both 1050A-H111 aluminum and 5182-H111 aluminum are aluminum alloys. Both are furnished in the H111 temper. They have a moderately high 95% of their average alloy composition in common.

For each property being compared, the top bar is 1050A-H111 aluminum and the bottom bar is 5182-H111 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 20
69
Elastic (Young's, Tensile) Modulus, GPa 68
68
Elongation at Break, % 26
12
Fatigue Strength, MPa 22
100
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
25
Shear Strength, MPa 49
170
Tensile Strength: Ultimate (UTS), MPa 76
280
Tensile Strength: Yield (Proof), MPa 23
130

Thermal Properties

Latent Heat of Fusion, J/g 400
390
Maximum Temperature: Mechanical, °C 170
180
Melting Completion (Liquidus), °C 660
640
Melting Onset (Solidus), °C 650
590
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 230
130
Thermal Expansion, µm/m-K 24
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 59
28
Electrical Conductivity: Equal Weight (Specific), % IACS 200
94

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
9.5
Density, g/cm3 2.7
2.7
Embodied Carbon, kg CO2/kg material 8.2
8.9
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1200
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 15
28
Resilience: Unit (Modulus of Resilience), kJ/m3 3.8
120
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
51
Strength to Weight: Axial, points 7.8
29
Strength to Weight: Bending, points 15
36
Thermal Diffusivity, mm2/s 94
53
Thermal Shock Resistance, points 3.4
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 99.5 to 100
93.2 to 95.8
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 0 to 0.050
0 to 0.15
Iron (Fe), % 0 to 0.4
0 to 0.35
Magnesium (Mg), % 0 to 0.050
4.0 to 5.0
Manganese (Mn), % 0 to 0.050
0.2 to 0.5
Silicon (Si), % 0 to 0.25
0 to 0.2
Titanium (Ti), % 0 to 0.050
0 to 0.1
Zinc (Zn), % 0 to 0.070
0 to 0.25
Residuals, % 0
0 to 0.15