1060 Aluminum vs. AWS ENiCrCoMo-1

1060 aluminum belongs to the aluminum alloys classification, while AWS ENiCrCoMo-1 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1060 aluminum and the bottom bar is AWS ENiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
210
Elongation at Break, % 1.1 to 30
28
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
82
Tensile Strength: Ultimate (UTS), MPa 67 to 130
710

Thermal Properties

Latent Heat of Fusion, J/g 400
330
Melting Completion (Liquidus), °C 660
1430
Melting Onset (Solidus), °C 650
1380
Specific Heat Capacity, J/kg-K 900
440
Thermal Expansion, µm/m-K 24
13

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
75
Density, g/cm3 2.7
8.5
Embodied Carbon, kg CO2/kg material 8.3
11
Embodied Energy, MJ/kg 160
140
Embodied Water, L/kg 1200
340

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
23
Strength to Weight: Axial, points 6.9 to 13
23
Strength to Weight: Bending, points 14 to 21
21
Thermal Shock Resistance, points 3.0 to 5.6
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 99.6 to 100
0
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
21 to 26
Cobalt (Co), % 0
9.0 to 15
Copper (Cu), % 0 to 0.050
0 to 0.5
Iron (Fe), % 0 to 0.35
0 to 5.0
Magnesium (Mg), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.030
0.3 to 2.5
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
38.6 to 61.7
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.25
0 to 0.75
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.050
0
Residuals, % 0
0 to 0.5