1060 Aluminum vs. Nickel 22

1060 aluminum belongs to the aluminum alloys classification, while nickel 22 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1060 aluminum and the bottom bar is nickel 22.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
220
Elongation at Break, % 1.1 to 30
49
Fatigue Strength, MPa 15 to 50
330
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
84
Shear Strength, MPa 42 to 75
560
Tensile Strength: Ultimate (UTS), MPa 67 to 130
790
Tensile Strength: Yield (Proof), MPa 17 to 110
360

Thermal Properties

Latent Heat of Fusion, J/g 400
320
Maximum Temperature: Mechanical, °C 170
990
Melting Completion (Liquidus), °C 660
1390
Melting Onset (Solidus), °C 650
1360
Specific Heat Capacity, J/kg-K 900
430
Thermal Conductivity, W/m-K 230
10
Thermal Expansion, µm/m-K 24
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 62
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 210
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
70
Density, g/cm3 2.7
8.9
Embodied Carbon, kg CO2/kg material 8.3
12
Embodied Energy, MJ/kg 160
170
Embodied Water, L/kg 1200
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 0.57 to 37
320
Resilience: Unit (Modulus of Resilience), kJ/m3 2.1 to 89
300
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
22
Strength to Weight: Axial, points 6.9 to 13
25
Strength to Weight: Bending, points 14 to 21
21
Thermal Diffusivity, mm2/s 96
2.7
Thermal Shock Resistance, points 3.0 to 5.6
24

Alloy Composition

Aluminum (Al), % 99.6 to 100
0
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
20 to 22.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.35
2.0 to 6.0
Magnesium (Mg), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.030
0 to 0.015
Molybdenum (Mo), % 0
12.5 to 14.5
Nickel (Ni), % 0
50.8 to 63
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0 to 0.25
0 to 0.080
Sulfur (S), % 0
0 to 0.020
Titanium (Ti), % 0 to 0.030
0
Tungsten (W), % 0
2.5 to 3.5
Vanadium (V), % 0 to 0.050
0 to 0.35
Zinc (Zn), % 0 to 0.050
0