1060 Aluminum vs. Nickel 689

1060 aluminum belongs to the aluminum alloys classification, while nickel 689 belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1060 aluminum and the bottom bar is nickel 689.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
210
Elongation at Break, % 1.1 to 30
23
Fatigue Strength, MPa 15 to 50
420
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
80
Shear Strength, MPa 42 to 75
790
Tensile Strength: Ultimate (UTS), MPa 67 to 130
1250
Tensile Strength: Yield (Proof), MPa 17 to 110
690

Thermal Properties

Latent Heat of Fusion, J/g 400
330
Maximum Temperature: Mechanical, °C 170
990
Melting Completion (Liquidus), °C 660
1440
Melting Onset (Solidus), °C 650
1390
Specific Heat Capacity, J/kg-K 900
450
Thermal Expansion, µm/m-K 24
12

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
70
Density, g/cm3 2.7
8.5
Embodied Carbon, kg CO2/kg material 8.3
11
Embodied Energy, MJ/kg 160
150
Embodied Water, L/kg 1200
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 0.57 to 37
240
Resilience: Unit (Modulus of Resilience), kJ/m3 2.1 to 89
1170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
23
Strength to Weight: Axial, points 6.9 to 13
41
Strength to Weight: Bending, points 14 to 21
30
Thermal Shock Resistance, points 3.0 to 5.6
35

Alloy Composition

Aluminum (Al), % 99.6 to 100
0.75 to 1.3
Boron (B), % 0
0.0030 to 0.010
Carbon (C), % 0
0.1 to 0.2
Chromium (Cr), % 0
18 to 20
Cobalt (Co), % 0
9.0 to 11
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.35
0 to 5.0
Magnesium (Mg), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.030
0 to 0.5
Molybdenum (Mo), % 0
9.0 to 10.5
Nickel (Ni), % 0
48.3 to 60.9
Phosphorus (P), % 0
0 to 0.015
Silicon (Si), % 0 to 0.25
0 to 0.5
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0 to 0.030
2.3 to 2.8
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.050
0