1070A Aluminum vs. 2195 Aluminum

Both 1070A aluminum and 2195 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is 1070A aluminum and the bottom bar is 2195 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
69
Elongation at Break, % 2.3 to 33
9.3
Fatigue Strength, MPa 17 to 51
190
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
26
Shear Strength, MPa 44 to 81
350
Tensile Strength: Ultimate (UTS), MPa 68 to 140
590
Tensile Strength: Yield (Proof), MPa 17 to 120
560

Thermal Properties

Latent Heat of Fusion, J/g 400
390
Maximum Temperature: Mechanical, °C 170
210
Melting Completion (Liquidus), °C 640
660
Melting Onset (Solidus), °C 640
550
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 230
130
Thermal Expansion, µm/m-K 23
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 60
34
Electrical Conductivity: Equal Weight (Specific), % IACS 200
100

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
31
Density, g/cm3 2.7
3.0
Embodied Carbon, kg CO2/kg material 8.2
8.6
Embodied Energy, MJ/kg 150
160
Embodied Water, L/kg 1200
1470

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 3.0 to 18
54
Resilience: Unit (Modulus of Resilience), kJ/m3 2.1 to 100
2290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
46
Strength to Weight: Axial, points 7.0 to 14
55
Strength to Weight: Bending, points 14 to 22
53
Thermal Diffusivity, mm2/s 94
49
Thermal Shock Resistance, points 3.1 to 6.3
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 99.7 to 100
91.9 to 94.9
Copper (Cu), % 0 to 0.030
3.7 to 4.3
Iron (Fe), % 0 to 0.25
0 to 0.15
Lithium (Li), % 0
0.8 to 1.2
Magnesium (Mg), % 0 to 0.030
0.25 to 0.8
Manganese (Mn), % 0 to 0.030
0 to 0.25
Silicon (Si), % 0 to 0.2
0 to 0.12
Silver (Ag), % 0
0.25 to 0.6
Titanium (Ti), % 0 to 0.030
0 to 0.1
Zinc (Zn), % 0 to 0.070
0 to 0.25
Zirconium (Zr), % 0
0.080 to 0.16
Residuals, % 0
0 to 0.15