1070A-H14 Aluminum vs. 4015-H14 Aluminum
Both 1070A-H14 aluminum and 4015-H14 aluminum are aluminum alloys. Both are furnished in the H14 temper. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is 1070A-H14 aluminum and the bottom bar is 4015-H14 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 32 | |
| 50 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 70 |
| Elongation at Break, % | 6.2 | |
| 2.9 |
| Fatigue Strength, MPa | 40 | |
| 63 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 69 | |
| 98 |
| Tensile Strength: Ultimate (UTS), MPa | 120 | |
| 170 |
| Tensile Strength: Yield (Proof), MPa | 79 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 640 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 230 | |
| 160 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 60 | |
| 41 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 200 | |
| 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 8.1 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1200 | |
| 1160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.5 | |
| 4.5 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 46 | |
| 130 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 12 | |
| 17 |
| Strength to Weight: Bending, points | 20 | |
| 25 |
| Thermal Diffusivity, mm2/s | 94 | |
| 66 |
| Thermal Shock Resistance, points | 5.2 | |
| 7.5 |
Alloy Composition
| Aluminum (Al), % | 99.7 to 100 | |
| 94.9 to 97.9 |
| Copper (Cu), % | 0 to 0.030 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0 to 0.030 | |
| 0.1 to 0.5 |
| Manganese (Mn), % | 0 to 0.030 | |
| 0.6 to 1.2 |
| Silicon (Si), % | 0 to 0.2 | |
| 1.4 to 2.2 |
| Titanium (Ti), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 to 0.070 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |