1200 Aluminum vs. EN-MC21230 Magnesium
1200 aluminum belongs to the aluminum alloys classification, while EN-MC21230 magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 1200 aluminum and the bottom bar is EN-MC21230 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 23 to 48 | |
| 63 |
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 45 |
| Elongation at Break, % | 1.1 to 28 | |
| 10 |
| Fatigue Strength, MPa | 25 to 69 | |
| 99 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 54 to 100 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 85 to 180 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 28 to 160 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 120 |
| Melting Completion (Liquidus), °C | 660 | |
| 600 |
| Melting Onset (Solidus), °C | 650 | |
| 520 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 1000 |
| Thermal Conductivity, W/m-K | 230 | |
| 72 |
| Thermal Expansion, µm/m-K | 23 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 58 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 190 | |
| 63 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1190 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.0 to 19 | |
| 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 5.7 to 180 | |
| 200 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 71 |
| Strength to Weight: Axial, points | 8.7 to 19 | |
| 36 |
| Strength to Weight: Bending, points | 16 to 26 | |
| 48 |
| Thermal Diffusivity, mm2/s | 92 | |
| 43 |
| Thermal Shock Resistance, points | 3.8 to 8.1 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 99 to 100 | |
| 5.5 to 8.5 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.010 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 | |
| 90.5 to 94.4 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0.1 to 0.6 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.010 |