ASTM D6456 Type II Class 1 vs. PTFE
ASTM D6456 type II class 1 belongs to the thermoset plastics classification, while PTFE belongs to the thermoplastics. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM D6456 type II class 1 and the bottom bar is PTFE.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 180 | |
| 6.9 to 24 |
| Elongation at Break, % | 4.0 | |
| 75 to 300 |
| Flexural Modulus, GPa | 3.1 | |
| 0.4 to 1.3 |
| Flexural Strength, MPa | 91 | |
| 13 to 50 |
| Tensile Strength: Ultimate (UTS), MPa | 61 | |
| 13 to 25 |
Thermal Properties
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 370 | |
| 66 to 70 |
| Maximum Temperature: Mechanical, °C | 260 | |
| 260 to 270 |
| Thermal Conductivity, W/m-K | 0.86 | |
| 0.24 to 0.65 |
| Thermal Expansion, µm/m-K | 49 | |
| 110 to 120 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 3.1 | |
| 2.1 to 2.4 |
| Electrical Dissipation At 1 MHz | 0.011 | |
| 0.00017 to 0.050 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 15 | |
| 2.0 to 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.5 | |
| 2.1 to 2.3 |
| Limiting Oxygen Index (LOI), % | 40 | |
| 90 |
| Water Absorption After 24 Hours, % | 0.19 | |
| 0.0093 to 0.050 |
Common Calculations
| Strength to Weight: Axial, points | 11 | |
| 1.7 to 3.2 |
| Strength to Weight: Bending, points | 23 | |
| 5.7 to 8.7 |