20 GF PC vs. ABS
Both 20 GF PC and ABS are thermoplastics. There are 14 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is 20 GF PC and the bottom bar is ABS.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 5.9 | |
| 2.0 to 2.6 |
| Elongation at Break, % | 5.5 | |
| 3.5 to 50 |
| Flexural Modulus, GPa | 5.7 | |
| 2.1 to 7.6 |
| Flexural Strength, MPa | 130 | |
| 72 to 97 |
| Impact Strength: Notched Izod, J/m | 140 | |
| 70 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 110 | |
| 37 to 110 |
Thermal Properties
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 150 | |
| 76 to 110 |
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 150 | |
| 83 to 110 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 19 | |
| 15 to 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 | |
| 1.0 to 1.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 2.4 | |
| 0.79 to 1.4 |
| Stiffness to Weight: Bending, points | 45 | |
| 30 to 44 |
| Strength to Weight: Axial, points | 23 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 38 | |
| 24 to 37 |