MakeItFrom.com
Menu (ESC)

201.0 Aluminum vs. 8079 Aluminum

Both 201.0 aluminum and 8079 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is 201.0 aluminum and the bottom bar is 8079 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
69
Elongation at Break, % 4.4 to 20
2.2
Fatigue Strength, MPa 120 to 150
56
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 27
26
Tensile Strength: Ultimate (UTS), MPa 370 to 470
150
Tensile Strength: Yield (Proof), MPa 220 to 400
120

Thermal Properties

Latent Heat of Fusion, J/g 390
400
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 650
650
Melting Onset (Solidus), °C 570
640
Specific Heat Capacity, J/kg-K 870
900
Thermal Conductivity, W/m-K 120
230
Thermal Expansion, µm/m-K 19
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 30 to 33
58
Electrical Conductivity: Equal Weight (Specific), % IACS 87 to 97
190

Otherwise Unclassified Properties

Base Metal Price, % relative 38
9.0
Density, g/cm3 3.1
2.8
Embodied Carbon, kg CO2/kg material 8.7
8.2
Embodied Energy, MJ/kg 160
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 63
3.1
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 1160
110
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 45
50
Strength to Weight: Axial, points 33 to 42
15
Strength to Weight: Bending, points 37 to 44
22
Thermal Diffusivity, mm2/s 45
92
Thermal Shock Resistance, points 19 to 25
6.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.1 to 95.1
98.1 to 99.3
Copper (Cu), % 4.0 to 5.2
0 to 0.050
Iron (Fe), % 0 to 0.15
0.7 to 1.3
Magnesium (Mg), % 0.15 to 0.55
0
Manganese (Mn), % 0.2 to 0.5
0
Silicon (Si), % 0 to 0.1
0.050 to 0.3
Silver (Ag), % 0.4 to 1.0
0
Titanium (Ti), % 0.15 to 0.35
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0 to 0.1
0 to 0.15