2011 Aluminum vs. EN 1.4539 Stainless Steel

2011 aluminum belongs to the aluminum alloys classification, while EN 1.4539 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 2011 aluminum and the bottom bar is EN 1.4539 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
200
Elongation at Break, % 8.5 to 18
38
Fatigue Strength, MPa 74 to 120
220
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 27
79
Shear Strength, MPa 190 to 250
430
Tensile Strength: Ultimate (UTS), MPa 310 to 420
630
Tensile Strength: Yield (Proof), MPa 140 to 310
260

Thermal Properties

Latent Heat of Fusion, J/g 390
300
Maximum Temperature: Mechanical, °C 190
1100
Melting Completion (Liquidus), °C 640
1440
Melting Onset (Solidus), °C 540
1390
Specific Heat Capacity, J/kg-K 870
460
Thermal Conductivity, W/m-K 140 to 170
12
Thermal Expansion, µm/m-K 23
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 35 to 45
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 100 to 130
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 11
31
Density, g/cm3 3.1
8.1
Embodied Carbon, kg CO2/kg material 7.9
5.7
Embodied Energy, MJ/kg 150
78
Embodied Water, L/kg 1150
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29 to 52
190
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 680
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 44
24
Strength to Weight: Axial, points 27 to 37
22
Strength to Weight: Bending, points 32 to 40
20
Thermal Diffusivity, mm2/s 51 to 64
3.2
Thermal Shock Resistance, points 14 to 19
14

Alloy Composition

Aluminum (Al), % 91.3 to 94.6
0
Bismuth (Bi), % 0.2 to 0.6
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
19 to 21
Copper (Cu), % 5.0 to 6.0
1.2 to 2.0
Iron (Fe), % 0 to 0.7
43.1 to 51.8
Lead (Pb), % 0.2 to 0.6
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 0
24 to 26
Nitrogen (N), % 0
0 to 0.15
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.7
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0