2011 Aluminum vs. S15700 Stainless Steel

2011 aluminum belongs to the aluminum alloys classification, while S15700 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 2011 aluminum and the bottom bar is S15700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
200
Elongation at Break, % 8.5 to 18
1.1 to 29
Fatigue Strength, MPa 74 to 120
370 to 770
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 27
77
Shear Strength, MPa 190 to 250
770 to 1070
Tensile Strength: Ultimate (UTS), MPa 310 to 420
1180 to 1890
Tensile Strength: Yield (Proof), MPa 140 to 310
500 to 1770

Thermal Properties

Latent Heat of Fusion, J/g 390
290
Maximum Temperature: Mechanical, °C 190
870
Melting Completion (Liquidus), °C 640
1440
Melting Onset (Solidus), °C 540
1400
Specific Heat Capacity, J/kg-K 870
480
Thermal Conductivity, W/m-K 140 to 170
16
Thermal Expansion, µm/m-K 23
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 35 to 45
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 100 to 130
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 11
15
Density, g/cm3 3.1
7.8
Embodied Carbon, kg CO2/kg material 7.9
3.4
Embodied Energy, MJ/kg 150
47
Embodied Water, L/kg 1150
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29 to 52
17 to 270
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 680
640 to 4660
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 44
25
Strength to Weight: Axial, points 27 to 37
42 to 67
Strength to Weight: Bending, points 32 to 40
32 to 43
Thermal Diffusivity, mm2/s 51 to 64
4.2
Thermal Shock Resistance, points 14 to 19
39 to 63

Alloy Composition

Aluminum (Al), % 91.3 to 94.6
0.75 to 1.5
Bismuth (Bi), % 0.2 to 0.6
0
Carbon (C), % 0
0 to 0.090
Chromium (Cr), % 0
14 to 16
Copper (Cu), % 5.0 to 6.0
0
Iron (Fe), % 0 to 0.7
69.6 to 76.8
Lead (Pb), % 0.2 to 0.6
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
6.5 to 7.7
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0