2017A Aluminum vs. 2618A Aluminum
Both 2017A aluminum and 2618A aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is 2017A aluminum and the bottom bar is 2618A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 72 |
| Elongation at Break, % | 2.2 to 14 | |
| 4.5 |
| Fatigue Strength, MPa | 92 to 130 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 27 |
| Shear Strength, MPa | 120 to 270 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 460 | |
| 440 |
| Tensile Strength: Yield (Proof), MPa | 110 to 290 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 230 |
| Melting Completion (Liquidus), °C | 650 | |
| 670 |
| Melting Onset (Solidus), °C | 510 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 880 |
| Thermal Conductivity, W/m-K | 150 | |
| 150 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 37 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 11 |
| Density, g/cm3 | 3.0 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 8.4 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1140 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.7 to 53 | |
| 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 to 570 | |
| 1180 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 47 |
| Strength to Weight: Axial, points | 19 to 42 | |
| 41 |
| Strength to Weight: Bending, points | 26 to 44 | |
| 44 |
| Thermal Diffusivity, mm2/s | 56 | |
| 59 |
| Thermal Shock Resistance, points | 8.9 to 20 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 91.3 to 95.5 | |
| 91.5 to 95.2 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 3.5 to 4.5 | |
| 1.8 to 2.7 |
| Iron (Fe), % | 0 to 0.7 | |
| 0.9 to 1.4 |
| Magnesium (Mg), % | 0.4 to 1.0 | |
| 1.2 to 1.8 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0 to 0.25 |
| Nickel (Ni), % | 0 | |
| 0.8 to 1.4 |
| Silicon (Si), % | 0.2 to 0.8 | |
| 0.15 to 0.25 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.15 |
| Zirconium (Zr), % | 0 to 0.25 | |
| 0 to 0.25 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |