2036 Aluminum vs. C87610 Bronze

2036 aluminum belongs to the aluminum alloys classification, while C87610 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 2036 aluminum and the bottom bar is C87610 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
110
Elongation at Break, % 24
22
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
43
Tensile Strength: Ultimate (UTS), MPa 340
350
Tensile Strength: Yield (Proof), MPa 200
140

Thermal Properties

Latent Heat of Fusion, J/g 390
270
Maximum Temperature: Mechanical, °C 190
190
Melting Completion (Liquidus), °C 650
970
Melting Onset (Solidus), °C 560
820
Specific Heat Capacity, J/kg-K 890
410
Thermal Conductivity, W/m-K 160
28
Thermal Expansion, µm/m-K 23
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 41
6.1
Electrical Conductivity: Equal Weight (Specific), % IACS 130
6.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
29
Density, g/cm3 2.9
8.5
Embodied Carbon, kg CO2/kg material 8.1
2.6
Embodied Energy, MJ/kg 150
43
Embodied Water, L/kg 1160
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
62
Resilience: Unit (Modulus of Resilience), kJ/m3 270
88
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 48
19
Strength to Weight: Axial, points 33
11
Strength to Weight: Bending, points 38
13
Thermal Diffusivity, mm2/s 62
8.1
Thermal Shock Resistance, points 15
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 97.4
0
Chromium (Cr), % 0 to 0.1
0
Copper (Cu), % 2.2 to 3.0
90 to 94
Iron (Fe), % 0 to 0.5
0 to 0.2
Lead (Pb), % 0
0 to 0.2
Magnesium (Mg), % 0.3 to 0.6
0
Manganese (Mn), % 0.1 to 0.4
0 to 0.25
Silicon (Si), % 0 to 0.5
3.0 to 5.0
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.25
3.0 to 5.0
Residuals, % 0 to 0.15
0 to 0.5