2219 Aluminum vs. AS41B Magnesium
2219 aluminum belongs to the aluminum alloys classification, while AS41B magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 2219 aluminum and the bottom bar is AS41B magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 45 |
| Elongation at Break, % | 2.2 to 20 | |
| 6.0 |
| Fatigue Strength, MPa | 90 to 130 | |
| 97 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 27 | |
| 18 |
| Shear Strength, MPa | 110 to 280 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 480 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 88 to 390 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 110 |
| Melting Completion (Liquidus), °C | 640 | |
| 620 |
| Melting Onset (Solidus), °C | 540 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 1000 |
| Thermal Conductivity, W/m-K | 110 to 170 | |
| 68 |
| Thermal Expansion, µm/m-K | 22 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 to 44 | |
| 17 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 81 to 130 | |
| 92 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 12 |
| Density, g/cm3 | 3.1 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1130 | |
| 980 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.6 to 60 | |
| 11 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 54 to 1060 | |
| 220 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 44 | |
| 72 |
| Strength to Weight: Axial, points | 16 to 43 | |
| 35 |
| Strength to Weight: Bending, points | 23 to 44 | |
| 47 |
| Thermal Diffusivity, mm2/s | 42 to 63 | |
| 41 |
| Thermal Shock Resistance, points | 8.2 to 22 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 91.5 to 93.8 | |
| 3.5 to 5.0 |
| Copper (Cu), % | 5.8 to 6.8 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.0035 |
| Magnesium (Mg), % | 0 to 0.020 | |
| 92.7 to 95.7 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0.35 to 0.7 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 0.2 | |
| 0.5 to 1.5 |
| Titanium (Ti), % | 0.020 to 0.1 | |
| 0 |
| Vanadium (V), % | 0.050 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.12 |
| Zirconium (Zr), % | 0.1 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |