238.0 Aluminum vs. EN 1.3555 Steel
238.0 aluminum belongs to the aluminum alloys classification, while EN 1.3555 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 238.0 aluminum and the bottom bar is EN 1.3555 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 76 | |
| 190 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 28 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 430 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 540 |
| Melting Completion (Liquidus), °C | 600 | |
| 1500 |
| Melting Onset (Solidus), °C | 510 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 840 | |
| 460 |
| Thermal Expansion, µm/m-K | 21 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 9.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 67 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 11 |
| Density, g/cm3 | 3.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 5.6 |
| Embodied Energy, MJ/kg | 140 | |
| 81 |
| Embodied Water, L/kg | 1040 | |
| 90 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 42 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 27 |
| Strength to Weight: Bending, points | 23 | |
| 23 |
| Thermal Shock Resistance, points | 9.1 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 81.9 to 84.9 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 0 | |
| 3.9 to 4.3 |
| Copper (Cu), % | 9.5 to 10.5 | |
| 0 to 0.1 |
| Iron (Fe), % | 1.0 to 1.5 | |
| 85.4 to 87.7 |
| Magnesium (Mg), % | 0 to 0.25 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.35 |
| Molybdenum (Mo), % | 0 | |
| 4.0 to 4.5 |
| Nickel (Ni), % | 0 | |
| 3.2 to 3.6 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 3.6 to 4.4 | |
| 0.1 to 0.25 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.15 |
| Vanadium (V), % | 0 | |
| 1.0 to 1.3 |
| Zinc (Zn), % | 1.0 to 1.5 | |
| 0 |