296.0 Aluminum vs. Titanium 15-3-3-3
296.0 aluminum belongs to the aluminum alloys classification, while titanium 15-3-3-3 belongs to the titanium alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 296.0 aluminum and the bottom bar is titanium 15-3-3-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 100 |
| Elongation at Break, % | 3.2 to 7.1 | |
| 5.7 to 8.0 |
| Fatigue Strength, MPa | 47 to 70 | |
| 610 to 710 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 270 | |
| 1120 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 120 to 180 | |
| 1100 to 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 430 |
| Melting Completion (Liquidus), °C | 630 | |
| 1620 |
| Melting Onset (Solidus), °C | 540 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 520 |
| Thermal Conductivity, W/m-K | 130 to 150 | |
| 8.1 |
| Thermal Expansion, µm/m-K | 22 | |
| 9.8 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 to 37 | |
| 1.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 to 110 | |
| 2.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 40 |
| Density, g/cm3 | 3.0 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 59 |
| Embodied Energy, MJ/kg | 150 | |
| 950 |
| Embodied Water, L/kg | 1110 | |
| 260 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.6 to 15 | |
| 78 to 89 |
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 46 | |
| 32 |
| Strength to Weight: Axial, points | 24 to 25 | |
| 64 to 80 |
| Strength to Weight: Bending, points | 30 to 31 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 51 to 56 | |
| 3.2 |
| Thermal Shock Resistance, points | 12 | |
| 79 to 98 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 89 to 94 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 2.5 to 3.5 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 1.2 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 |
| Nickel (Ni), % | 0 to 0.35 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.13 |
| Silicon (Si), % | 2.0 to 3.0 | |
| 0 |
| Tin (Sn), % | 0 | |
| 2.5 to 3.5 |
| Titanium (Ti), % | 0 to 0.25 | |
| 72.6 to 78.5 |
| Vanadium (V), % | 0 | |
| 14 to 16 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.35 | |
| 0 to 0.4 |