296.0 Aluminum vs. Titanium 6-7
296.0 aluminum belongs to the aluminum alloys classification, while titanium 6-7 belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is 296.0 aluminum and the bottom bar is titanium 6-7.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 120 |
| Elongation at Break, % | 3.2 to 7.1 | |
| 11 |
| Fatigue Strength, MPa | 47 to 70 | |
| 530 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 270 | |
| 1020 |
| Tensile Strength: Yield (Proof), MPa | 120 to 180 | |
| 900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 300 |
| Melting Completion (Liquidus), °C | 630 | |
| 1700 |
| Melting Onset (Solidus), °C | 540 | |
| 1650 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 520 |
| Thermal Expansion, µm/m-K | 22 | |
| 9.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 75 |
| Density, g/cm3 | 3.0 | |
| 5.1 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 34 |
| Embodied Energy, MJ/kg | 150 | |
| 540 |
| Embodied Water, L/kg | 1110 | |
| 190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.6 to 15 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 220 | |
| 3460 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 32 |
| Strength to Weight: Axial, points | 24 to 25 | |
| 56 |
| Strength to Weight: Bending, points | 30 to 31 | |
| 44 |
| Thermal Shock Resistance, points | 12 | |
| 66 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 89 to 94 | |
| 5.5 to 6.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0090 |
| Iron (Fe), % | 0 to 1.2 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 6.5 to 7.5 |
| Nickel (Ni), % | 0 to 0.35 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 6.5 to 7.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 2.0 to 3.0 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 to 0.25 | |
| 84.9 to 88 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.35 | |
| 0 |