H03 C12500 Copper vs. H03 C24000 Brass
Both H03 C12500 copper and H03 C24000 brass are copper alloys. Both are furnished in the H03 (3/4 hard) temper. They have 80% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is H03 C12500 copper and the bottom bar is H03 C24000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 330 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 160 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1000 |
| Melting Onset (Solidus), °C | 1070 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 350 | |
| 140 |
| Thermal Expansion, µm/m-K | 17 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 92 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 93 | |
| 34 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 27 |
| Density, g/cm3 | 8.9 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 41 | |
| 43 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 10 | |
| 15 |
| Strength to Weight: Bending, points | 12 | |
| 16 |
| Thermal Diffusivity, mm2/s | 100 | |
| 43 |
| Thermal Shock Resistance, points | 12 | |
| 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Antimony (Sb), % | 0 to 0.0030 | |
| 0 |
| Arsenic (As), % | 0 to 0.012 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.0030 | |
| 0 |
| Copper (Cu), % | 99.88 to 100 | |
| 78.5 to 81.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.0040 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 to 0.050 | |
| 0 |
| Tellurium (Te), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 18.2 to 21.5 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.2 |