30 CF PEEK vs. 6061-T6 Aluminum
30 CF PEEK and 6061-T6 aluminum belong to fundamentally different material chemistries. 30 CF PEEK is a polymeric material, while 6061-T6 aluminum is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 16 material properties with values for both materials. Properties with values for just one material (29, in this case) are not shown.
For each property being compared, the top bar is 30 CF PEEK and the bottom bar is 6061-T6 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 24 | |
| 69 |
| Elongation at Break, % | 1.6 | |
| 10 |
| Shear Strength, MPa | 100 | |
| 210 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 310 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 330 | |
| 170 |
| Melting Onset (Solidus), °C | 340 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 1520 | |
| 900 |
| Thermal Conductivity, W/m-K | 0.93 | |
| 170 |
| Thermal Expansion, µm/m-K | 15 | |
| 24 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.5 | |
| 14 |
| Stiffness to Weight: Bending, points | 69 | |
| 50 |
| Strength to Weight: Axial, points | 41 | |
| 31 |
| Strength to Weight: Bending, points | 55 | |
| 37 |
| Thermal Diffusivity, mm2/s | 0.44 | |
| 68 |
| Thermal Shock Resistance, points | 40 | |
| 14 |