319.0 Aluminum vs. 6023 Aluminum
Both 319.0 aluminum and 6023 aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 319.0 aluminum and the bottom bar is 6023 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 69 |
| Elongation at Break, % | 1.8 to 2.0 | |
| 11 |
| Fatigue Strength, MPa | 76 to 80 | |
| 120 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 170 to 210 | |
| 210 to 220 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 240 | |
| 360 |
| Tensile Strength: Yield (Proof), MPa | 110 to 180 | |
| 300 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 480 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 600 | |
| 640 |
| Melting Onset (Solidus), °C | 540 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 890 |
| Thermal Conductivity, W/m-K | 110 | |
| 170 |
| Thermal Expansion, µm/m-K | 22 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 84 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 11 |
| Density, g/cm3 | 2.9 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 8.3 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1080 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.3 to 3.9 | |
| 38 to 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 88 to 220 | |
| 670 to 690 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 48 | |
| 49 |
| Strength to Weight: Axial, points | 18 to 24 | |
| 35 to 36 |
| Strength to Weight: Bending, points | 25 to 30 | |
| 40 |
| Thermal Diffusivity, mm2/s | 44 | |
| 67 |
| Thermal Shock Resistance, points | 8.6 to 11 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 85.8 to 91.5 | |
| 94 to 97.7 |
| Bismuth (Bi), % | 0 | |
| 0.3 to 0.8 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0.2 to 0.5 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 to 0.1 | |
| 0.4 to 0.9 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.2 to 0.6 |
| Nickel (Ni), % | 0 to 0.35 | |
| 0 |
| Silicon (Si), % | 5.5 to 6.5 | |
| 0.6 to 1.4 |
| Tin (Sn), % | 0 | |
| 0.6 to 1.2 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.15 |