324.0 Aluminum vs. 242.0 Aluminum
Both 324.0 aluminum and 242.0 aluminum are aluminum alloys. They have a moderately high 92% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is 324.0 aluminum and the bottom bar is 242.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 73 |
| Elongation at Break, % | 3.0 to 4.0 | |
| 0.5 to 1.5 |
| Fatigue Strength, MPa | 77 to 89 | |
| 55 to 110 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 310 | |
| 180 to 290 |
| Tensile Strength: Yield (Proof), MPa | 110 to 270 | |
| 120 to 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 500 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 210 |
| Melting Completion (Liquidus), °C | 610 | |
| 640 |
| Melting Onset (Solidus), °C | 550 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 870 |
| Thermal Conductivity, W/m-K | 150 | |
| 130 to 170 |
| Thermal Expansion, µm/m-K | 21 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 33 to 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 96 to 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1090 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.8 to 8.9 | |
| 1.3 to 3.4 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 85 to 510 | |
| 110 to 340 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 52 | |
| 45 |
| Strength to Weight: Axial, points | 22 to 32 | |
| 16 to 26 |
| Strength to Weight: Bending, points | 29 to 38 | |
| 23 to 32 |
| Thermal Diffusivity, mm2/s | 62 | |
| 50 to 62 |
| Thermal Shock Resistance, points | 9.7 to 14 | |
| 8.0 to 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 87.3 to 92.2 | |
| 88.4 to 93.6 |
| Chromium (Cr), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 0.4 to 0.6 | |
| 3.5 to 4.5 |
| Iron (Fe), % | 0 to 1.2 | |
| 0 to 1.0 |
| Magnesium (Mg), % | 0.4 to 0.7 | |
| 1.2 to 1.8 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.35 |
| Nickel (Ni), % | 0 to 0.3 | |
| 1.7 to 2.3 |
| Silicon (Si), % | 7.0 to 8.0 | |
| 0 to 0.7 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 to 0.35 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.15 |