324.0 Aluminum vs. EN AC-44100 Aluminum

Both 324.0 aluminum and EN AC-44100 aluminum are aluminum alloys. They have a very high 95% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 324.0 aluminum and the bottom bar is EN AC-44100 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
72
Elongation at Break, % 3.0 to 4.0
4.9
Fatigue Strength, MPa 77 to 89
64
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 27
27
Tensile Strength: Ultimate (UTS), MPa 210 to 310
180
Tensile Strength: Yield (Proof), MPa 110 to 270
87

Thermal Properties

Latent Heat of Fusion, J/g 500
570
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 610
590
Melting Onset (Solidus), °C 550
580
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 150
130
Thermal Expansion, µm/m-K 21
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 34
34
Electrical Conductivity: Equal Weight (Specific), % IACS 120
120

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.5
Embodied Carbon, kg CO2/kg material 7.9
7.7
Embodied Energy, MJ/kg 150
140
Embodied Water, L/kg 1090
1050

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.8 to 8.9
7.1
Resilience: Unit (Modulus of Resilience), kJ/m3 85 to 510
53
Stiffness to Weight: Axial, points 15
16
Stiffness to Weight: Bending, points 52
55
Strength to Weight: Axial, points 22 to 32
19
Strength to Weight: Bending, points 29 to 38
27
Thermal Diffusivity, mm2/s 62
58
Thermal Shock Resistance, points 9.7 to 14
8.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.3 to 92.2
84.4 to 89.5
Copper (Cu), % 0.4 to 0.6
0 to 0.15
Iron (Fe), % 0 to 1.2
0 to 0.65
Lead (Pb), % 0
0 to 0.1
Magnesium (Mg), % 0.4 to 0.7
0 to 0.1
Manganese (Mn), % 0 to 0.5
0 to 0.55
Nickel (Ni), % 0 to 0.3
0 to 0.1
Silicon (Si), % 7.0 to 8.0
10.5 to 13.5
Titanium (Ti), % 0 to 0.2
0 to 0.2
Zinc (Zn), % 0 to 1.0
0 to 0.15
Residuals, % 0 to 0.2
0 to 0.15