3303 aluminum belongs to the aluminum alloys classification, while AWS BCo-1 belongs to the cobalt alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 3303 aluminum and the bottom bar is AWS BCo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
200
Poisson's Ratio 0.33
0.3
Shear Modulus, GPa 26
78
Tensile Strength: Ultimate (UTS), MPa 110
700

Thermal Properties

Latent Heat of Fusion, J/g 400
420
Melting Completion (Liquidus), °C 650
1150
Melting Onset (Solidus), °C 620
1120
Specific Heat Capacity, J/kg-K 900
480
Thermal Expansion, µm/m-K 23
12

Otherwise Unclassified Properties

Density, g/cm3 2.8
8.1
Embodied Carbon, kg CO2/kg material 8.1
8.0
Embodied Energy, MJ/kg 150
110
Embodied Water, L/kg 1180
430

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 49
24
Strength to Weight: Axial, points 11
24
Strength to Weight: Bending, points 18
22
Thermal Shock Resistance, points 4.8
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 96.6 to 99
0 to 0.050
Boron (B), % 0
0.7 to 0.9
Carbon (C), % 0
0.35 to 0.45
Chromium (Cr), % 0
18 to 20
Cobalt (Co), % 0
46 to 54
Copper (Cu), % 0.050 to 0.2
0
Iron (Fe), % 0 to 0.7
0 to 1.0
Manganese (Mn), % 1.0 to 1.5
0
Nickel (Ni), % 0
16 to 18
Phosphorus (P), % 0
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 0.6
7.5 to 8.5
Sulfur (S), % 0
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0
3.5 to 4.5
Zinc (Zn), % 0 to 0.3
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0 to 0.15
0 to 0.5