3303 Aluminum vs. CC499K Bronze

3303 aluminum belongs to the aluminum alloys classification, while CC499K bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 3303 aluminum and the bottom bar is CC499K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
110
Elongation at Break, % 23
13
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
41
Tensile Strength: Ultimate (UTS), MPa 110
260
Tensile Strength: Yield (Proof), MPa 39
120

Thermal Properties

Latent Heat of Fusion, J/g 400
190
Maximum Temperature: Mechanical, °C 180
170
Melting Completion (Liquidus), °C 650
1000
Melting Onset (Solidus), °C 620
920
Specific Heat Capacity, J/kg-K 900
370
Thermal Conductivity, W/m-K 170
73
Thermal Expansion, µm/m-K 23
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 43
12
Electrical Conductivity: Equal Weight (Specific), % IACS 140
12

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
32
Density, g/cm3 2.8
8.8
Embodied Carbon, kg CO2/kg material 8.1
3.1
Embodied Energy, MJ/kg 150
51
Embodied Water, L/kg 1180
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 20
27
Resilience: Unit (Modulus of Resilience), kJ/m3 11
65
Stiffness to Weight: Axial, points 14
6.9
Stiffness to Weight: Bending, points 49
18
Strength to Weight: Axial, points 11
8.1
Strength to Weight: Bending, points 18
10
Thermal Diffusivity, mm2/s 67
22
Thermal Shock Resistance, points 4.8
9.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 96.6 to 99
0 to 0.010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.020
Cadmium (Cd), % 0
0 to 0.020
Chromium (Cr), % 0
0 to 0.020
Copper (Cu), % 0.050 to 0.2
84 to 88
Iron (Fe), % 0 to 0.7
0 to 0.3
Lead (Pb), % 0
0 to 3.0
Manganese (Mn), % 1.0 to 1.5
0
Nickel (Ni), % 0
0 to 0.6
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 0.010
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 0
4.0 to 6.0
Zinc (Zn), % 0 to 0.3
4.0 to 6.0
Residuals, % 0 to 0.15
0