3303 Aluminum vs. CR009A Copper

3303 aluminum belongs to the aluminum alloys classification, while CR009A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 3303 aluminum and the bottom bar is CR009A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
120
Elongation at Break, % 23
15
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
43
Tensile Strength: Ultimate (UTS), MPa 110
230
Tensile Strength: Yield (Proof), MPa 39
140

Thermal Properties

Latent Heat of Fusion, J/g 400
210
Maximum Temperature: Mechanical, °C 180
200
Melting Completion (Liquidus), °C 650
1090
Melting Onset (Solidus), °C 620
1040
Specific Heat Capacity, J/kg-K 900
390
Thermal Conductivity, W/m-K 170
380
Thermal Expansion, µm/m-K 23
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 43
100
Electrical Conductivity: Equal Weight (Specific), % IACS 140
100

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
31
Density, g/cm3 2.8
9.0
Embodied Carbon, kg CO2/kg material 8.1
2.6
Embodied Energy, MJ/kg 150
41
Embodied Water, L/kg 1180
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 20
31
Resilience: Unit (Modulus of Resilience), kJ/m3 11
83
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 49
18
Strength to Weight: Axial, points 11
7.1
Strength to Weight: Bending, points 18
9.3
Thermal Diffusivity, mm2/s 67
110
Thermal Shock Resistance, points 4.8
8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 96.6 to 99
0
Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Cadmium (Cd), % 0
0 to 0.00010
Copper (Cu), % 0.050 to 0.2
99.99 to 100
Iron (Fe), % 0 to 0.7
0 to 0.0010
Lead (Pb), % 0
0 to 0.00050
Manganese (Mn), % 1.0 to 1.5
0 to 0.00050
Nickel (Ni), % 0
0 to 0.0010
Phosphorus (P), % 0
0 to 0.0030
Selenium (Se), % 0
0 to 0.00020
Silicon (Si), % 0 to 0.6
0
Silver (Ag), % 0
0 to 0.0025
Sulfur (S), % 0
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020
Tin (Sn), % 0
0 to 0.00020
Zinc (Zn), % 0 to 0.3
0 to 0.00010
Residuals, % 0 to 0.15
0