3303 Aluminum vs. C19000 Copper

3303 aluminum belongs to the aluminum alloys classification, while C19000 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 3303 aluminum and the bottom bar is C19000 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
120
Elongation at Break, % 23
2.5 to 50
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
43
Shear Strength, MPa 69
170 to 390
Tensile Strength: Ultimate (UTS), MPa 110
260 to 760
Tensile Strength: Yield (Proof), MPa 39
140 to 630

Thermal Properties

Latent Heat of Fusion, J/g 400
210
Maximum Temperature: Mechanical, °C 180
200
Melting Completion (Liquidus), °C 650
1080
Melting Onset (Solidus), °C 620
1040
Specific Heat Capacity, J/kg-K 900
390
Thermal Conductivity, W/m-K 170
250
Thermal Expansion, µm/m-K 23
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 43
60
Electrical Conductivity: Equal Weight (Specific), % IACS 140
61

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
31
Density, g/cm3 2.8
8.9
Embodied Carbon, kg CO2/kg material 8.1
2.7
Embodied Energy, MJ/kg 150
42
Embodied Water, L/kg 1180
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 20
18 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 11
89 to 1730
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 49
18
Strength to Weight: Axial, points 11
8.2 to 24
Strength to Weight: Bending, points 18
10 to 21
Thermal Diffusivity, mm2/s 67
73
Thermal Shock Resistance, points 4.8
9.3 to 27

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 96.6 to 99
0
Copper (Cu), % 0.050 to 0.2
96.9 to 99
Iron (Fe), % 0 to 0.7
0 to 0.1
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 1.0 to 1.5
0
Nickel (Ni), % 0
0.9 to 1.3
Phosphorus (P), % 0
0.15 to 0.35
Silicon (Si), % 0 to 0.6
0
Zinc (Zn), % 0 to 0.3
0 to 0.8
Residuals, % 0 to 0.15
0 to 0.5