3303 Aluminum vs. C82200 Copper

3303 aluminum belongs to the aluminum alloys classification, while C82200 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 3303 aluminum and the bottom bar is C82200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
120
Elongation at Break, % 23
8.0 to 20
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
44
Tensile Strength: Ultimate (UTS), MPa 110
390 to 660
Tensile Strength: Yield (Proof), MPa 39
210 to 520

Thermal Properties

Latent Heat of Fusion, J/g 400
220
Maximum Temperature: Mechanical, °C 180
230
Melting Completion (Liquidus), °C 650
1080
Melting Onset (Solidus), °C 620
1040
Specific Heat Capacity, J/kg-K 900
390
Thermal Conductivity, W/m-K 170
180
Thermal Expansion, µm/m-K 23
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 43
45
Electrical Conductivity: Equal Weight (Specific), % IACS 140
46

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
55
Density, g/cm3 2.8
8.9
Embodied Carbon, kg CO2/kg material 8.1
4.8
Embodied Energy, MJ/kg 150
74
Embodied Water, L/kg 1180
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 20
49 to 66
Resilience: Unit (Modulus of Resilience), kJ/m3 11
180 to 1130
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 49
18
Strength to Weight: Axial, points 11
12 to 20
Strength to Weight: Bending, points 18
13 to 19
Thermal Diffusivity, mm2/s 67
53
Thermal Shock Resistance, points 4.8
14 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 96.6 to 99
0
Beryllium (Be), % 0
0.35 to 0.8
Cobalt (Co), % 0
0 to 0.3
Copper (Cu), % 0.050 to 0.2
97.4 to 98.7
Iron (Fe), % 0 to 0.7
0
Manganese (Mn), % 1.0 to 1.5
0
Nickel (Ni), % 0
1.0 to 2.0
Silicon (Si), % 0 to 0.6
0
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0 to 0.5