336.0 Aluminum vs. 1050A Aluminum

Both 336.0 aluminum and 1050A aluminum are aluminum alloys. They have 83% of their average alloy composition in common.

For each property being compared, the top bar is 336.0 aluminum and the bottom bar is 1050A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 130
20 to 45
Elastic (Young's, Tensile) Modulus, GPa 75
68
Elongation at Break, % 0.5
1.1 to 33
Fatigue Strength, MPa 80 to 93
22 to 55
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 28
26
Shear Strength, MPa 190 to 250
44 to 97
Tensile Strength: Ultimate (UTS), MPa 250 to 320
68 to 170
Tensile Strength: Yield (Proof), MPa 190 to 300
22 to 150

Thermal Properties

Latent Heat of Fusion, J/g 570
400
Maximum Temperature: Mechanical, °C 210
170
Melting Completion (Liquidus), °C 570
660
Melting Onset (Solidus), °C 540
650
Specific Heat Capacity, J/kg-K 890
900
Thermal Conductivity, W/m-K 120
230
Thermal Expansion, µm/m-K 19
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 29
59
Electrical Conductivity: Equal Weight (Specific), % IACS 95
200

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.0
Density, g/cm3 2.8
2.7
Embodied Carbon, kg CO2/kg material 7.9
8.2
Embodied Energy, MJ/kg 140
150
Embodied Water, L/kg 1010
1200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 1.1 to 1.6
1.9 to 19
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 580
3.7 to 160
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 51
50
Strength to Weight: Axial, points 25 to 32
6.9 to 18
Strength to Weight: Bending, points 32 to 38
14 to 25
Thermal Diffusivity, mm2/s 48
94
Thermal Shock Resistance, points 12 to 16
3.0 to 7.6

Alloy Composition

Aluminum (Al), % 79.1 to 85.8
99.5 to 100
Copper (Cu), % 0.5 to 1.5
0 to 0.050
Iron (Fe), % 0 to 1.2
0 to 0.4
Magnesium (Mg), % 0.7 to 1.3
0 to 0.050
Manganese (Mn), % 0 to 0.35
0 to 0.050
Nickel (Ni), % 2.0 to 3.0
0
Silicon (Si), % 11 to 13
0 to 0.25
Titanium (Ti), % 0 to 0.25
0 to 0.050
Zinc (Zn), % 0 to 0.35
0 to 0.070