336.0 Aluminum vs. 5021 Aluminum
Both 336.0 aluminum and 5021 aluminum are aluminum alloys. They have 84% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 336.0 aluminum and the bottom bar is 5021 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 75 | |
| 68 |
| Elongation at Break, % | 0.5 | |
| 1.1 to 3.4 |
| Fatigue Strength, MPa | 80 to 93 | |
| 85 to 110 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 28 | |
| 26 |
| Shear Strength, MPa | 190 to 250 | |
| 170 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 320 | |
| 300 to 310 |
| Tensile Strength: Yield (Proof), MPa | 190 to 300 | |
| 240 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 570 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 180 |
| Melting Completion (Liquidus), °C | 570 | |
| 640 |
| Melting Onset (Solidus), °C | 540 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 900 |
| Thermal Conductivity, W/m-K | 120 | |
| 140 |
| Thermal Expansion, µm/m-K | 19 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 2.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 8.6 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1010 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.1 to 1.6 | |
| 3.1 to 10 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 580 | |
| 440 to 550 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 50 |
| Strength to Weight: Axial, points | 25 to 32 | |
| 30 to 32 |
| Strength to Weight: Bending, points | 32 to 38 | |
| 37 |
| Thermal Diffusivity, mm2/s | 48 | |
| 57 |
| Thermal Shock Resistance, points | 12 to 16 | |
| 13 to 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 79.1 to 85.8 | |
| 95.2 to 97.7 |
| Chromium (Cr), % | 0 | |
| 0 to 0.15 |
| Copper (Cu), % | 0.5 to 1.5 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 to 1.2 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.7 to 1.3 | |
| 2.2 to 2.8 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.1 to 0.5 |
| Nickel (Ni), % | 2.0 to 3.0 | |
| 0 |
| Silicon (Si), % | 11 to 13 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.35 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |