336.0 Aluminum vs. 7075 Aluminum
Both 336.0 aluminum and 7075 aluminum are aluminum alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 336.0 aluminum and the bottom bar is 7075 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 75 | |
| 70 |
| Elongation at Break, % | 0.5 | |
| 1.8 to 12 |
| Fatigue Strength, MPa | 80 to 93 | |
| 110 to 190 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 28 | |
| 26 |
| Shear Strength, MPa | 190 to 250 | |
| 150 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 320 | |
| 240 to 590 |
| Tensile Strength: Yield (Proof), MPa | 190 to 300 | |
| 120 to 510 |
Thermal Properties
| Latent Heat of Fusion, J/g | 570 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 200 |
| Melting Completion (Liquidus), °C | 570 | |
| 640 |
| Melting Onset (Solidus), °C | 540 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 870 |
| Thermal Conductivity, W/m-K | 120 | |
| 130 |
| Thermal Expansion, µm/m-K | 19 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 98 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 10 |
| Density, g/cm3 | 2.8 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 8.3 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1010 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.1 to 1.6 | |
| 7.8 to 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 580 | |
| 110 to 1870 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 46 |
| Strength to Weight: Axial, points | 25 to 32 | |
| 22 to 54 |
| Strength to Weight: Bending, points | 32 to 38 | |
| 28 to 52 |
| Thermal Diffusivity, mm2/s | 48 | |
| 50 |
| Thermal Shock Resistance, points | 12 to 16 | |
| 10 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 79.1 to 85.8 | |
| 86.9 to 91.4 |
| Chromium (Cr), % | 0 | |
| 0.18 to 0.28 |
| Copper (Cu), % | 0.5 to 1.5 | |
| 1.2 to 2.0 |
| Iron (Fe), % | 0 to 1.2 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.7 to 1.3 | |
| 2.1 to 2.9 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 0.3 |
| Nickel (Ni), % | 2.0 to 3.0 | |
| 0 |
| Silicon (Si), % | 11 to 13 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.35 | |
| 5.1 to 6.1 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |