354.0 Aluminum vs. EN 1.4436 Stainless Steel

354.0 aluminum belongs to the aluminum alloys classification, while EN 1.4436 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 354.0 aluminum and the bottom bar is EN 1.4436 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
200
Elongation at Break, % 2.4 to 3.0
42
Fatigue Strength, MPa 92 to 120
220
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 27
78
Tensile Strength: Ultimate (UTS), MPa 360 to 380
620
Tensile Strength: Yield (Proof), MPa 280 to 310
240

Thermal Properties

Latent Heat of Fusion, J/g 530
290
Maximum Temperature: Mechanical, °C 170
960
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 550
1400
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 130
15
Thermal Expansion, µm/m-K 21
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 110
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
19
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 7.8
3.9
Embodied Energy, MJ/kg 150
54
Embodied Water, L/kg 1070
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 8.6 to 9.8
210
Resilience: Unit (Modulus of Resilience), kJ/m3 540 to 670
150
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 52
25
Strength to Weight: Axial, points 37 to 39
22
Strength to Weight: Bending, points 42 to 44
20
Thermal Diffusivity, mm2/s 52
4.0
Thermal Shock Resistance, points 17 to 18
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 87.3 to 89.4
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
16.5 to 18.5
Copper (Cu), % 1.6 to 2.0
0
Iron (Fe), % 0 to 0.2
62.3 to 70.5
Magnesium (Mg), % 0.4 to 0.6
0
Manganese (Mn), % 0 to 0.1
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.0
Nickel (Ni), % 0
10.5 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 8.6 to 9.4
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.1
0
Residuals, % 0 to 0.15
0