358.0 Aluminum vs. 7108 Aluminum
Both 358.0 aluminum and 7108 aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common.
For each property being compared, the top bar is 358.0 aluminum and the bottom bar is 7108 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 69 |
| Elongation at Break, % | 3.5 to 6.0 | |
| 11 |
| Fatigue Strength, MPa | 100 to 110 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 300 to 320 | |
| 210 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 370 | |
| 350 |
| Tensile Strength: Yield (Proof), MPa | 290 to 320 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 520 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 210 |
| Melting Completion (Liquidus), °C | 600 | |
| 630 |
| Melting Onset (Solidus), °C | 560 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 880 |
| Thermal Conductivity, W/m-K | 150 | |
| 150 |
| Thermal Expansion, µm/m-K | 21 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 | |
| 39 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 9.5 |
| Density, g/cm3 | 2.6 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 8.3 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1090 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 20 | |
| 38 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 590 to 710 | |
| 620 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 53 | |
| 47 |
| Strength to Weight: Axial, points | 37 to 39 | |
| 34 |
| Strength to Weight: Bending, points | 42 to 44 | |
| 38 |
| Thermal Diffusivity, mm2/s | 63 | |
| 59 |
| Thermal Shock Resistance, points | 16 to 17 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 89.1 to 91.8 | |
| 92.4 to 94.7 |
| Beryllium (Be), % | 0.1 to 0.3 | |
| 0 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0.7 to 1.4 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.050 |
| Silicon (Si), % | 7.6 to 8.6 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0.1 to 0.2 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.2 | |
| 4.5 to 5.5 |
| Zirconium (Zr), % | 0 | |
| 0.12 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |